Yb: YAG laser welding of dual phase steel to aluminium alloy
Santhanakrishnan Soundarapandian, Lakshmanan Vijayaraghavan
Published in Elsevier Ltd
2018
Volume: 262
   
Pages: 411 - 421
Abstract
In this work, laser welding of dual phase steel (DP 600) to aluminium alloy (AA 6061) was studied both experimentally and by computational modeling. Three different laser energy densities (640 J/mm2, 850 J/mm2 and 1250 J/mm2) were chosen to study the effect of heat input on microstructural changes and strength of the joint. It was inferred from the results that the laser energy density had a direct influence on the formation of intermetallic phases such as Fe2Al5 and FeAl3. At relatively high laser energy density (1250 J/mm2), thick intermetallic layer and crack propagations were observed at the interface of the weld, which deteriorated the strength of joint. Whereas, maintaining the laser energy density at 850 J/mm2 enhanced the weld quality by lowering the intermetallic thickness in the range of 6–10 μm and defects such as cracks were also lowest at the weld interface. The formation of the cracks in the interfacial region was largely influenced by the hard and brittle intermetallics, which was evident from the microhardness results. The microhardness value along the interface exhibited a maximum of 836 HV at 1250 J/mm2, which was much higher than the base metal hardness (AA 6061 – 65 HV, DP 600 - 255 HV). A two-dimensional computational model was used to predict the temperature histories at different laser energy densities during welding. The results of the computational model (penetration depth and material ablation) correlated well with the experimental results. © 2018 Elsevier B.V.
About the journal
JournalData powered by TypesetJournal of Materials Processing Technology
PublisherData powered by TypesetElsevier Ltd
ISSN09240136
Open AccessNo
Concepts (21)
  •  related image
    Aluminum
  •  related image
    Binary alloys
  •  related image
    Computation theory
  •  related image
    Computational methods
  •  related image
    Cracks
  •  related image
    Heat affected zone
  •  related image
    High strength steel
  •  related image
    INTERMETALLICS
  •  related image
    Laser beam welding
  •  related image
    Microhardness
  •  related image
    SOLDERING ALLOYS
  •  related image
    YTTRIUM ALUMINUM GARNET
  •  related image
    Advanced high strength steel
  •  related image
    DUAL-PHASE STEEL
  •  related image
    INTERMETALLIC LAYER
  •  related image
    Intermetallic phasis
  •  related image
    INTERMETALLIC THICKNESS
  •  related image
    Laser energy density
  •  related image
    Microstructural changes
  •  related image
    TWO-DIMENSIONAL COMPUTATIONAL MODELS
  •  related image
    Aluminum alloys