Stepwise Depletion of Coating Elements as a Result of Hot Corrosion of NiCrAlY Coatings
, Rana Nidhi, Satya Prakash
Published in Springer Science and Business Media LLC
2014
Volume: 23
   
Issue: 2
Pages: 643 - 650
Abstract

Present investigation deals with the hot corrosion behaviour of the NiCrAlY coatings deposited by HVOF technique on Superni76 under cyclic conditions at 900 °C in the presence of Na2SO4 + 60% V2O5 salt. The weight change behaviour of the coatings was followed with time up to 200 cycles and K p value was calculated for the hot corrosion process. Surface and cross-section of the corroded samples were examined by FESEM/EDS and XRD to follow the progress of corrosion up to 200 cycles. In earlier cycles, the corrosive species oxidised top surface of the coatings. With increasing number of cycles, oxidation of the coatings occurred up to 40-μm depth. A Cr-depleted band was seen below the oxide scale. Further increase in number of cycles led to migration and oxidation of Al to form Al2O3 sublayer at coating/scale interface, thereby leading to formation of Al-depleted zone in the coating below the Al2O3 sublayer. The corrosion resistance of the NiCrAlY coatings is attributed to the formation of the continuous and dense Al2O3 sublayer at the coating/scale interface, which acts as barrier to the migration of Cr to the surface. The appearance of Al3Y after 100 and 200 cycles also contributes to the increased corrosion resistance of coatings after 100 and 200 cycles.

About the journal
PublisherData powered by TypesetSpringer Science and Business Media LLC
Open AccessNo