Halide perovskites show incredible photovoltaic power conversion efficiency coupled with several hundreds of hours of device stability. However, their stability is poor in aqueous electrolyte media. Reported here is a vacancy ordered halide perovskite, Cs₂PtI₆, which shows extraordinary stability under ambient conditions (1 year), in aqueous media of extreme acidic (pH 1), basic (pH 13), and under electrochemical reduction conditions. It was employed as an electrocatalyst and photoanode for hydrogen production and water oxidation, respectively. The catalyst remains intact for at least 100 cycles of electrochemical cycling and six hours of hydrogen production at pH 1. Cs₂PtI₆ was employed as a photoanode for PEC water oxidation, and the material displayed a photocurrent of 0.8 mA cm⁻² at 1.23 V (vs. RHE) under simulated AM1.5G sunlight. Using constant voltage measurement, Cs₂PtI₆ exhibited over 12 hours of PEC stability without loss of performance.